在加工行业及手板打样中，喷砂是一件非常常用的表面处理工艺，其实很多人都不知道该如何选择手板表面处理中喷砂。所以接下来由济南手板厂家为大家进行简单地介绍。

In the processing industry and hand plate proofing, sandblasting is a very common surface treatment process. In fact, many people do not know how to choose sandblasting in hand plate surface treatment. So let's have a brief introduction from Jinan Handboard Factory.

喷砂加工范围：五金除锈、铝合金喷砂、玻璃喷砂（雾面效果）、塑胶喷砂（去毛边）、亚克力喷砂（雾面效果）、PC、PS表面处理、树脂表面处理、铸造工件喷砂、锌合金喷砂（粗糙面）、不锈钢材料喷砂、石材料喷砂、五金除油漆、五金件除焊疤、抛丸、等配件表面处理。

Sand blasting processing scope: metal rust removal, aluminum alloy sand blasting, glass sand blasting (fog surface effect), plastic sand blasting (deburring), acrylic sand blasting (fog surface effect), PC, PS surface treatment, resin surface treatment, casting workpiece sand blasting, zinc alloy sand blasting (rough surface), stainless steel material sand blasting, stone material sand blasting, metal paint removal, metal parts welding scar removal, shot blasting, and other accessories surface treatment.

亚克力喷砂：如果客户要求很雾，一般喷玻璃砂，如果要求高一点可以选用白刚玉。如果要求不是很雾有一定透明性就须选用玻璃珠，有时候会玻璃珠里加一点玻璃砂，这样喷出来的效果就是是有一点点透的。

Acrylic sand blasting: if the customer requires fog, glass sand is generally sprayed. If the requirement is higher, white corundum can be used. If it is not required to be foggy and transparent, glass beads must be selected. Sometimes a little glass sand will be added to the glass beads, so that the effect of spraying is a little transparent.

不锈钢喷砂：一般需要了解不锈钢是什么样的面板，有抛光面合金钢丸，拉丝面什么是合金钢，还有原板的雾面，需要粗糙度的，对表面平滑度没有要求的，可以选用棕刚玉和白刚玉，有特殊要求，需要光滑的，选用玻璃珠和玻璃砂。

Stainless steel sandblasting: generally, you need to know what kind of stainless steel is, including polished surface alloy steel shot, brushed surface alloy steel, and fog surface of the original plate. If roughness is required, but there is no requirement for surface smoothness, you can choose brown corundum and white corundum. If there are special requirements and need to be smooth, you can choose glass beads and glass sand.

压铸件：一般都是是去除毛刺低合金钢，一般都可以使用抛丸机低合金钢什么是合金钢，使用铸钢丸钢珠，使用钢珠钢丸喷砂抛丸物体表面擦伤少，刮痕浅和小，对于去除表面污物多厚的选用钢砂，一般可考虑钢珠和钢砂混合使用。如果想使得喷砂的铝件颜色更白一些高合金钢什么是合金钢，应该考虑使用成本高的不锈钢丸、钢丝切丸，如果想节省成本，考虑铸钢珠和不休钢丸按8：2的比例混合使用，喷砂抛丸时每工作一次便将钢珠清洗一次，多喷砂抛丸几次也可达到比较白的效果。

Die castings: generally, it is low alloy steel with burr removal. Generally, shot blasting machine can be used to remove low alloy steel. What is alloy steel? Cast steel shot and steel ball can be used. The surface of shot blasting object with steel ball and steel shot is less scratched, and the scratch is shallow and small. For removal of thick surface dirt, steel sand can be selected. Generally, the mixed use of steel ball and steel sand can be considered. If you want to make the aluminum parts sandblasted whiter, what is alloy steel, you should consider using stainless steel shot and steel wire cut shot with high cost. If you want to save costs, you should consider using cast steel ball and continuous steel shot in the ratio of 8:2. When sandblasting, the steel ball will be cleaned once every time you work, and more sandblasting can also achieve a whiter effect.

以上内容便是手板表面处理中喷砂的选用，希望能够对大家有所帮助。如果想要了解更多关于手板的相关内容，我们将竭诚为大家服务http://m.metferro.com。

The above content is about the selection of sandblasting in the surface treatment of the hand board. I hope it can help you. If you want to know more about the hand board, we will serve you wholeheartedly http://m.metferro.com 。